Synthesis and Consolidation of Ternary Compound Ti3SiC2 from Green Compact of Mixed Powders
-
- Sun Zheng Ming
- National Institute of Advanced Industrial Science and Technology (AIST Tohoku)
-
- Yang Songlan
- National Institute of Advanced Industrial Science and Technology (AIST Tohoku)
-
- Hashimoto Hitoshi
- National Institute of Advanced Industrial Science and Technology (AIST Tohoku)
-
- Tada Shuji
- National Institute of Advanced Industrial Science and Technology (AIST Tohoku)
-
- Abe Toshihiko
- National Institute of Advanced Industrial Science and Technology (AIST Tohoku)
書誌事項
- タイトル別名
-
- Synthesis and Consolidation of Ternary Compound Ti<SUB>3</SUB>SiC<SUB>2</SUB> from Green Compact of Mixed Powders
この論文をさがす
抄録
Ternary compound Ti3SiC2 has been successfully synthesized and concurrently consolidated by sintering green compact of starting powder mixture. 3Ti/SiC/C powder mixture was compacted and heated in vacuum or in Ar atmosphere at temperatures from 1573 to 1773 K for a time period ranged from 2 to 6 hours. It has been found that either in vacuum or in Ar atmosphere the Ti3SiC2 content reached 100% in the surface layer. The growth of Ti3SiC2 in a layered manner on the surface of the sample was observed. It was also found that the sample sintered in Ar atmosphere is denser than those sintered in vacuum. After sintered in Ar atmosphere at 1773 K for 2 hours, the relative density of the compound reached 97%. Occurrence of liquid phase during sintering contributed to the densification of the compound.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 45 (2), 373-375, 2004
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679228443264
-
- NII論文ID
- 10012643425
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD2cXjt1Oqt74%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 6865583
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可