Eutectic Alloys in the Sn-Zn-Mg-Al System with Eutectic Temperature of 454 K

• Inada Masanori

  Formerly, Electronics Research Laboratory, Matsushita Electronics Corporation

• Kibe Masaki

  Formerly, Electronics Research Laboratory, Matsushita Electronics Corporation

抄録

We have experimentally found a Sn-Zn-Mg₂Sn eutectic alloy with the eutectic composition of 82Sn-10Zn-8Mg (mol%) and with nearly the same eutectic temperature of 454 K as that of the Pb-Sn eutectic alloy. The eutectic alloy was made in air by covering Sn, Zn and Mg with the 59KCl-41LiCl (mol%) composition eutectic melt in an Al₂O₃ crucible, melting the metals at 1073 K and washing away the alkali-chlorides with distilled water after cooling to room temperature. The as-cast alloy easily oxidized at temperatures above 503 K in air after melting. It was found that the Sn-Zn-(Mg, Al)₂Sn eutectic alloys that were made by replacing 0.8 to 4.0 mol% of Mg with Al in the ternary eutectic composition with the same alloying method did not oxidize in air after melting.

収録刊行物

• MATERIALS TRANSACTIONS

  MATERIALS TRANSACTIONS 45 (3), 790-792, 2004

  公益社団法人 日本金属学会

キーワード

• alloying method in air
• lead-free eutectic alloys
• tin-zinc-magnesium system
• tin-zinc-magnesium-aluminum system

詳細情報

• CRID: 1390001204251512576
• NII論文ID: 130004452378
• NII論文ID: 10012717080
• NII書誌ID: AA1151294X
• DOI: 10.2320/matertrans.45.790
• COI: 1:CAS:528:DC%2BD2cXjsVGru78%3D
• ISSN: 13475320
• ISSN: 13459678
• NDL書誌ID: 6899088
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I6899088
• Web Site: https://www.jstage.jst.go.jp/article/matertrans/45/3/45_3_790/_pdf
• 本文言語コード: en
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可