Mechanical Properties Related to Microstructural Variation of 6061 Al Alloy Joints by Friction Stir Welding

この論文にアクセスする

この論文をさがす

著者

抄録

The microstructural change related with the mechanical properties of a friction stir welded 6061 Al alloy has been investigated under various welding conditions. Frictional heat and plastic flow during friction stir welding produced fine and equiaxed grains in the stir zone, macroscopically upset and elongated grains in the thermo-mechanically affected zone caused by dynamic recovery and recrystallization. The heat-affected zone, characterized by coarse precipitates, was formed beside the weld zone. Hardness distribution near the weld zone was strongly related to the behavior of precipitates and dislocation density. Especially, hardness of the SZ at a higher tool rotation speed was higher than that of a lower tool rotation speed due to higher density of spherical shaped re-precipitates. The joint strength was approximately 200 MPa which was lower than that of the base metal, 270 MPa, because softening region was formed around the weld zone.

収録刊行物

  • Materials transactions

    Materials transactions 45(5), 1700-1705, 2004-05-20

    公益社団法人 日本金属学会

参考文献:  30件中 1-30件 を表示

各種コード

  • NII論文ID(NAID)
    10013071866
  • NII書誌ID(NCID)
    AA1151294X
  • 本文言語コード
    ENG
  • 資料種別
    ART
  • ISSN
    13459678
  • NDL 記事登録ID
    6951586
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z53-J286
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ