高温乾燥したスギ心材のオオウズラタケに対する耐朽性 Durability of Sugi (Cryptomeria japonica D. Don) Heartwood Dried at High Temperature against the Brown-rot Fungus Fomitopsis palustris

この論文にアクセスする

この論文をさがす

著者

抄録

100℃以上の高温乾燥がスギの耐朽性に及ぼす影響を検討した。オオウズラタケによる室内強制腐朽試験の結果,天然乾燥したスギや60~70℃で中温乾燥したスギ材の心材の質量減少率はいずれも約3%であったが,高温乾燥したスギでは27~35%に達し,高温乾燥による耐朽性の低下が示唆された。今後,野外試験により,高温乾燥したスギの耐用年数を確認する必要がある。

Durability of Sugi (Cryptomeria japonica D. Don) heartwood dried over 100°C was investigated with laboratory decay test. As the results of the decay test with Fomitopsis palustris, mass losses of the specimens from Sugi heartwood, which were air dried, or kiln-dried at 60 to 70'C, were approximately 3 %, while those of the heartwood dreid at high-temperature were 27 to 35%. Thus, decrease in durabilty of Sugi heartwood by high-temperature drying was suggested. Therefore, service life of high-temperature dried wood must be clarified by field tests.

収録刊行物

  • 木材保存 = Wood preservation

    木材保存 = Wood preservation 27(2), 61-66, 2001-03-25

    JAPAN WOOD PRESERVING ASSOCIATION

参考文献:  20件中 1-20件 を表示

被引用文献:  7件中 1-7件 を表示

各種コード

  • NII論文ID(NAID)
    10013233488
  • NII書誌ID(NCID)
    AN00240373
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    02879255
  • NDL 記事登録ID
    5729080
  • NDL 雑誌分類
    ZP21(科学技術--化学・化学工業--木材)
  • NDL 請求記号
    Z17-745
  • データ提供元
    CJP書誌  CJP引用  NDL  J-STAGE 
ページトップへ