Effect of Mechanical Vibration on the Microstructure, Impact Toughness and Thermal Fatigue Behavior of Cast Hot Working Die Steel

この論文にアクセスする

この論文をさがす

著者

    • ZHAO Y. G.
    • Department of Materials Science and Engineering, Jilin University at Nanling Campus
    • LIANG Y. H.
    • Department of Materials Science and Engineering, Jilin University at Nanling Campus
    • QIN Q. D.
    • Department of Materials Science and Engineering, Jilin University at Nanling Campus
    • ZHOU W.
    • Department of Materials Science and Engineering, Jilin University at Nanling Campus
    • JIANG Q. C.
    • The key Laboratory of Automobile Materials, Ministry of Education, Jilin University

抄録

The cast hot working die steel is treated by mechanical vibration (MV) with a frequency of 50 Hz during the solidification process. The experimental results indicate that the MV may break off the dendrites growing from mould wall towards center in the steel during solidification. Therefore, the growth of the dendrites is restrained and the microstructure in the steel is refined; furthermore, MV can decrease the amount of defects such as shrinkage cavity and inclusion and enhance the compactness of the steel. The impact toughness of the steel treated with MV is as 1.5 times larger as that of the untreated steel. During thermal fatigue (TF) test, it is found that TF crack is longer and wider and the chap are more severe in the untreated steel than in the steel treated with MV. Simultaneously, the average velocity of crack propagation is 1.7 times faster in the untreated steel than in the steel treated with MV.

収録刊行物

  • ISIJ international

    ISIJ international 44(7), 1167-1172, 2004-07-15

    The Iron and Steel Institute of Japan

参考文献:  19件中 1-19件 を表示

  • <no title>

    CSER L.

    Proc. Inst. Mech. Eng. 207, 223, 1993

    被引用文献2件

  • <no title>

    STARLING C. M.

    Thin. Solid. Films 308, 436, 1997

    被引用文献2件

  • <no title>

    MALM S.

    J. Mater. Sci. 9, 544, 1979

    被引用文献1件

  • <no title>

    JAHN R.

    British Patent No. 456 657, 1935

    被引用文献1件

  • <no title>

    OHNO A.

    Tetsu-to-Hagane 55, 475, 1969

    被引用文献1件

  • <no title>

    OHNO A.

    Tetsu-to-Hagane 56, 230, 1970

    被引用文献1件

  • <no title>

    HATAMURA Y.

    Tetsu-to-Hagane 72, 2978, 1986

    被引用文献1件

  • <no title>

    WU W. T.

    Scr. Mater. 42, 661, 2000

    被引用文献1件

  • <no title>

    SCHMIDT C.

    Z. Electrochem 43, 869, 1937

    被引用文献1件

  • <no title>

    LI G. B.

    J. Mater. Process. Technol. 100, 63, 2000

    被引用文献1件

  • <no title>

    SHUJ J.

    J. Journal. Industrial News Co 6, 24, 1974

    被引用文献1件

  • <no title>

    NAVINSEKA B.

    Surf. Coat. Technol. 142, 1148, 2001

    被引用文献1件

  • <no title>

    JIANG Q.

    Scr. Mater. 45, 199, 2001

    被引用文献2件

  • <no title>

    ZUCHOWSKI R.

    J. Mater. Process. Technol. 106, 167, 2000

    被引用文献1件

  • <no title>

    REVEL P.

    Mater. Sci. Eng. 290A, 25, 2000

    被引用文献1件

  • Microstructures and Thermal Fatigue Behavior of Cr-Ni-Mo Hot Work Die Steel Modified by Rare Earth

    GUAN Q. F. , JIANG Q. C. , FANG J. R. , JIANG H.

    ISIJ international 43(5), 784-789, 2003-05-15

    J-STAGE 参考文献20件 被引用文献4件

  • <no title>

    CARAM R.

    J. Cryst. Growth 114, 249, 1991

    被引用文献1件

  • <no title>

    WANG F.

    J. Mater. Sci. 29, 3997, 1994

    被引用文献1件

  • <no title>

    MENZEMER C. C.

    Mater. Sci. Eng. 289A, 198, 2000

    被引用文献1件

各種コード

ページトップへ