The Static and Metadynamic Recrystallization Behaviour of an X60 Nb Microalloyed Steel

この論文にアクセスする

この論文をさがす

著者

抄録

A rapid method has been developed to determine recrystallization kinetics of Nb microalloyed steels by interrupted hot torsion test. The softening behaviour was achieved as a function of different processing parameters. The method clearly identified three regions, where the strain dependency of the recrystallization rate varied. Firstly, at large strains the rate of recrystallization was not a function of strain; this is generally ascribed to metadynamic recrystallization. At lower strains the time to 50% recrystallization showed a power low relationship with strain, characteristic of static recrystallization. A further break point exists on the time for 50% softening curve when strain induced precipitation occurs in the material. The onset of strain induced precipitation was at strains below the strain to the peak stress at temperatures below 900°C. The experimental results were used to estimate the time for 50% softening and to anticipate the onset of the strain induced precipitation for the alloy of this study. Grain refinement of the recrystallized austenite continued to strains significantly beyond the peak stress and beyond the static to metadynamic recrystallization rate transition.

収録刊行物

  • ISIJ international

    ISIJ international 44(7), 1224-1229, 2004-07-15

    一般社団法人 日本鉄鋼協会

参考文献:  15件中 1-15件 を表示

  • <no title>

    JONAS J. J.

    Mater. Sci. Eng. A184, 155, 1994

    被引用文献2件

  • <no title>

    JONAS J. J.

    Metall. Reviews 14, 1, 1969

    被引用文献2件

  • <no title>

    DUTTA B.

    Mater. Sci. Technol. 3, 197, 1987

    被引用文献23件

  • <no title>

    HODGSON P. D.

    Mater. Forum 17, 403, 1993

    被引用文献3件

  • <no title>

    HODGSON P. D.

    ISIJ Int. 32, 1329, 1992

    被引用文献24件

  • <no title>

    JONAS J. J.

    Met. Sci. 13, 238, 1979

    被引用文献2件

  • <no title>

    HODGSON P. D.

    Proc. of 7th Int. Symp. on Physical Simulation, 1997 219, 1997

    被引用文献1件

  • <no title>

    FIELDS D. S.

    Proc. ASTM 57, 1259, 1957

    被引用文献3件

  • <no title>

    ROUCOULES C.

    Metall. Mater. Trans. A 25A, 389, 1994

    被引用文献4件

  • <no title>

    ASTM standards, E112-84, 02-01 1124, 1986

    被引用文献1件

  • <no title>

    POLIAK E. I.

    ISIJ Int. 43, 684, 2003

    被引用文献5件

  • <no title>

    MEDINA S. F.

    ISIJ Int. 41, 774, 2001

    被引用文献3件

  • <no title>

    JONAS J. J.

    Proc. of Thermomechanical Processing : Mechanics, 2002 23, 2002

    被引用文献1件

  • <no title>

    ZAHIRI S. H.

    Mater. Sci. Technol.

    被引用文献1件

  • <no title>

    CHO S.-H.

    ISIJ Int. 41, 63, 2001

    被引用文献4件

各種コード

ページトップへ