Fe-Ni合金の変則型電析機構の検討 Mechanism of Anomalous Electrodeposition of Fe-Ni

この論文にアクセスする

この論文をさがす

著者

抄録

Electrodeposition of Fe-Ni alloys was conducted galvanostatically in sulfate baths of pH 1-3 at 40<sup>º</sup>C to investigate their codeposition mechanism. The results obtained are described as follows : <br> (1) The electrodeposition behavior of Fe-Ni alloy showed a typical feature of anomalous codepostion, in which electrochemically less noble Fe deposits preferentially under most plating conditions. This anomalous codepostion was caused by the suppression of Ni deposition due to codeposition of Fe.<br> (2) The anomalous codeposition was evidently dependent on the pH buffer capacity of the baths, which can be explained in terms of the preferential adsorption of FeOH on the deposition sites due to different dissociation constants between FeOH<sup>+</sup> and NiOH<sup>+</sup> in the multi-step reduction process of hydrated iron-group metal ions.<br> (3) The degree of the preferential deposition of less noble Fe was decreased under the plating conditions to decrease the adsorption of FeOH on the cathode.<br> (4) The pH titration curves were measured in an Fe<sup>2+</sup> single bath using NaOH solution. The Fe<sup>2+</sup> -single bath showed pH buffering action around pH 6.3, which corresponds to FeOH<sup>+</sup> formation in the titration curve calculated from the dissociation constant of FeOH<sup>+</sup>.<br>

収録刊行物

  • 表面技術 = The Journal of the Surface Finishing Society of Japan

    表面技術 = The Journal of the Surface Finishing Society of Japan 55(6), 428-433, 2004-06-01

    一般社団法人 表面技術協会

参考文献:  21件中 1-21件 を表示

  • <no title>

    逢坂哲彌

    湿式法を利用したエレクトロニクス高機能薄膜製法 4, 1992

    被引用文献1件

  • <no title>

    毛利佳年雄

    磁気センサ理工学 1, 1998

    被引用文献1件

  • <no title>

    DAHMS H.

    J. Electrochem. Soc. 112, 771, 1965

    被引用文献17件

  • <no title>

    HORKANS J.

    J. Electrochem. Soc. 128, 45, 1981

    被引用文献2件

  • <no title>

    安田誠之

    金属表面技術 33, 427, 1982

    被引用文献3件

  • <no title>

    GRANDE W.C.

    J. Electrochem. Soc. 140, 669, 1993

    被引用文献5件

  • <no title>

    SASAKI K. Y.

    J. Electrochem. Soc. 142, 775, 1995

    被引用文献3件

  • <no title>

    MATLOSZ M.

    J. Electrochem. Soc. 140, 2272, 1993

    被引用文献4件

  • <no title>

    福島久哲

    金属表面技術 33, 574, 1982

    被引用文献8件

  • <no title>

    BARD A. J.

    溶液内イオン平衡 196, 1975

    被引用文献1件

  • <no title>

    BRENNER A.

    Electrodeposition of Alloys Vol. 1 & 2, 41,76, 1963

    被引用文献13件

  • <no title>

    BRENNER A.

    Electrodeposition of Alloys Vol.2, chap. 34, 1963

    被引用文献5件

  • <no title>

    FUKUSHIMA H.

    ISIJ Int. 33, 1009, 1993

    被引用文献7件

  • <no title>

    BOCKRIS J. O.

    J. Electrochem. Soc. 108, 676, 1961

    被引用文献1件

  • <no title>

    安田光宏

    表面技術 41, 312, 1990

    被引用文献5件

  • <no title>

    大上悟

    表面技術 53, 920, 1982

    被引用文献1件

  • めっき技術を用いた高密度ディスクおよび薄膜ヘッド (エレクトロニクスと表面処理技術特集号)

    菅沼 葉二 , 後藤 文男 , 逢坂 哲弥

    金属表面技術 34(6), p254-260, 1983-06

    被引用文献2件

  • <no title>

    HESSAMI S.

    J. Electrochem. Soc. 136, 3611, 1989

    DOI 被引用文献11件

  • <no title>

    LEHMAN E. B.

    Surface Technology 11, 349, 1980

    DOI 被引用文献1件

  • <no title>

    BAKER B. C.

    J. Electrochem. Soc. 144, 164-171, 1997

    被引用文献3件

  • <no title>

    VAES J.

    J. Electrochem. Soc. 147, 3718-3724, 2000

    被引用文献3件

各種コード

  • NII論文ID(NAID)
    10013272286
  • NII書誌ID(NCID)
    AN1005202X
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    09151869
  • NDL 記事登録ID
    7029920
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-291
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ