マグネシウム合金AZ31B板と1050アルミニウム板のAgインサートを用いた抵抗スポット溶接 Resistance spot welding of a magnesium alloy AZ31B plate to a 1050 aluminum plate using Ag insert metal

この論文にアクセスする

この論文をさがす

著者

抄録

In this study, resistance spot welding was applied to make a dissimilar-metal joint between Mg alloy AZ31B plate and commercially pure Al plate. Factors affecting the cross tensile strength of the joint and the effect of Ag insert on the joint strength were investigated. The main results obtained in this study are as follows.<br>The strength of the dissimilar-metal joint of Mg/Al increased with increasing welding current, however, the strength was very low and was about one forth to one fifth that of the similar-metal joint of Mg/Mg made under the same condition.<br>By using insert metal consisting of four layers of Ag foil with 0.1 mm thickness, the strength of the Mg/Ag joint increased about 1.5 times than that of the Mg/Ag joint without the insert metal.<br>With increase in the thickness of the foil-layered Ag insert metal, the thickness of an intermetallic compound formed at the interface between Mg and Ag decreased and the thickness of a eutectic reaction layer between Ag and Al increased, resulting in the increase in the Mg/Al joint strength. However, when the insert metal of 5-layers Ag foil was used, the strength of the Mg/Ag joint decreased because non-bonded regions occurred in the eutectic reaction layer.

収録刊行物

  • 軽金属

    軽金属 54(7), 293-297, 2004-07-30

    一般社団法人 軽金属学会

参考文献:  3件中 1-3件 を表示

  • <no title>

    小島陽

    金属 71, 494, 2001

    被引用文献3件

  • <no title>

    ASM

    Binary Alloy Phase Diagrams, 1996

    被引用文献2件

  • <no title>

    池内建二

    BOUNDARY 10, 2, 1988

    被引用文献1件

被引用文献:  2件中 1-2件 を表示

各種コード

  • NII論文ID(NAID)
    10013341827
  • NII書誌ID(NCID)
    AN00069773
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    04515994
  • NDL 記事登録ID
    7047731
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-284
  • データ提供元
    CJP書誌  CJP引用  NDL  J-STAGE 
ページトップへ