高分子水溶液で湿った多孔体の対流乾燥による含水率および含高分子率分布の経時変化 Profiles of Moisture and Polymer Content in Porous Material Wetted with Aqueous Polymer Solution upon Convective Drying

この論文にアクセスする

この論文をさがす

著者

抄録

ポリビニルアルコール(PVA)水溶液で湿ったガラス微粒子層の対流乾燥を行い,材料内の含水率と含PVA率分布の経時変化および乾燥速度を,初期含溶液率を変えて測定した.低初期含溶液率のときは,水で湿った場合と同様に蒸発面後退が起こり,PVAの移動も生じなかったが,高初期含溶液率のときは,乾燥初期に多量のPVAが表面近くに移動しそこで蓄積することで定率乾燥期間が現れず,低含水率域での蒸発面後退も認められなかった.

Convective dryingof a glass particle layer wetted with aqueous polyvinylalcohol (PVA) solution was examined. Profiles of moisture and PVA content in the layer during drying and the drying rate were measured for different initial solution contents. With a low initial content, a receding drying front was observed in the same way as in the layer wetted with water, and there was no PVA movement. With a high initial content, the receding front was not observed in the low content region, and much PVA moved toward the drying surface in the early period of drying and stayed there after. The PVA disturbed the drying and there was no constant rate period.

収録刊行物

  • 化学工学論文集

    化学工学論文集 28(4), 478-480, 2002-07-20

    公益社団法人 化学工学会

参考文献:  2件中 1-2件 を表示

被引用文献:  4件中 1-4件 を表示

各種コード

  • NII論文ID(NAID)
    10013409317
  • NII書誌ID(NCID)
    AN00037234
  • 本文言語コード
    JPN
  • 資料種別
    NOT
  • ISSN
    0386216X
  • NDL 記事登録ID
    6240556
  • NDL 雑誌分類
    ZP5(科学技術--化学・化学工業--化学工学)
  • NDL 請求記号
    Z17-725
  • データ提供元
    CJP書誌  CJP引用  NDL  J-STAGE 
ページトップへ