表面処理した浮上スライダのはつ油性と粘着低減効果 Oil-repellent Performance of a Surface-treated Flying Slider : The Stiction Reduction Effect

この論文にアクセスする

この論文をさがす

著者

抄録

磁気ヘッドを搭載する浮上スライダと磁気ディスクとの粘着を低減するため,スライダに各種表面処理を施した.1mass%のフルオロカーボン系シリコンアルコキシド溶液に浸漬/加熱処理したスライダの鉱油接触角はほぼ70° となった.この浸漬/加熱プロセスで処理したスライダを磁気ディスク装置で実装試験した結果,未処理スライダに比べて粘着力が約80%低減し,表面処理の粘着低減効果を確認した.また,この処理の前にスライダ表面に紫外線照射した場合はほぼ80° となり接触角が増大した.

To reduce the stiction between a magnetic disk and a flying slider carrying a magnetic head in a hard disk drive, the slider was subjected to surface treatment. Namely, the slider was dipped in 1 mass% FAS solution (2-(heptadecafluorooctyl)-ethyltrimethoxysilane) and heated to 393 K (i.e., a dipping/heating process). The mineral-oil contact angle on the slider after this treatment was 72 degrees. A read/write test was performed with the treated slider, and the stiction force on the treated slider was found to be decreased by about 80%, compared with that of an untreated slider. This result confirmed that the surface treatment effectively reduces stiction. Moreover, by irradiating the slider surface with ultraviolet light before the dipping/heating process, the contact angle was increased to about 80 degrees. It is also confirmed that ultraviolet light irradiation effectively reduces the stiction between the slider and disk.

収録刊行物

  • 化学工学論文集

    化学工学論文集 29(6), 748-752, 2003-11-20

    公益社団法人 化学工学会

参考文献:  10件中 1-10件 を表示

各種コード

  • NII論文ID(NAID)
    10013411592
  • NII書誌ID(NCID)
    AN00037234
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    0386216X
  • NDL 記事登録ID
    6776732
  • NDL 雑誌分類
    ZP5(科学技術--化学・化学工業--化学工学)
  • NDL 請求記号
    Z17-725
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ