- Shape Control of Rectangular Tube Castings Produced by Fused Spinning Deposition Method
- ヨウユウ タイセキホウ ニ ヨリ サクセイ シタ カクトウ セキソウザイ ノ ケイジョウ セイギョ
この論文をさがす
抄録
Al-4 mass%Cu alloy was melted in a quartz tube with a small nozzle at the bottom. By pressing the melt surface with argon gas pressure of 0.12 to 0.13 MPa, the alloy melt flowed out through the nozzle onto the copper substrate and was rapidly solidified. A rectangular tube specimen was formed by moving the sub. strate in the X-Y horizontal directions and downwards simultaneously. <br> With increasing the moving speed of the substrate, the thickness of one layer deposited reduced and the spacing between eutectics in the interdendritic regions increased, while the width of the castings remained almost constant. With increasing the number of layers, the cooling rate was decreased, and the weldability between the layers improved. Under optimum conditions, a coexisting solid-liquid region was formed between the layers, resulting in smooth side surface of the castings due to the surface tension of the liquid phase in the region.
収録刊行物
-
- 鋳造工学
-
鋳造工学 76 (7), 582-587, 2004
公益社団法人 日本鋳造工学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681484355840
-
- NII論文ID
- 130004556506
- 10013436279
-
- NII書誌ID
- AN10514770
-
- ISSN
- 21855374
- 13420429
-
- NDL書誌ID
- 7032834
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可