アルミニウム合金の半凝固接合プロセス

• 滝田 光晴

  名古屋大学大学院工学研究科

• 赤松 栄作

  名古屋大学大学院工学研究科

• 野村 宏之

  名古屋大学大学院工学研究科

書誌事項

タイトル別名

• Semi-Solid Joining Process of Aluminum Alloy
• アルミニウム ゴウキン ノ ハンギョウコ セツゴウ プロセス

抄録

  The semi-solid joining process of aluminum alloy was investigated. Hyper eutectic Al-25 mass% Si alloy was melted in an electric furnace. The melt was stirred with a ceramic stirrer while cooling. The stirrer was then changed to an aluminum insert (A2017) and stirring was continued for the duration of the semi-solid temperature region. After solidification, specimens were quenched into water and sectioned for analysis of macro- and micro-structures along the weld region. The area ratio of un-bonded, melt-down and normal bonded area were measured. Effects of insertion temperature, rotation time, rotation speed, and surface conditions of specimen on bonded area ratio were reviewed. EPMA line analysis data and calculated concentration of copper were also studied, and the influence of rotation conditions on shear strength was investigated. The research shows that cast-in aluminum alloy materials can be obtained by optimizing the surface conditions of insert material, stirring temperature, and time of semi-solid processing.

収録刊行物

• 鋳造工学

  鋳造工学 75 (6), 385-390, 2003

  公益社団法人 日本鋳造工学会

キーワード

• semi-solid
• aluminum alloy
• joining process
• rotation
• cast-in

詳細情報

• CRID: 1390282681482781568
• NII論文ID: 130004556472
• NII論文ID: 10013907532
• NII書誌ID: AN10514770
• DOI: 10.11279/jfes.75.385
• ISSN: 21855374
• ISSN: 13420429
• NDL書誌ID: 6615717
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I6615717
• 本文言語コード: en
• データソース種別:
  • JaLC
  • NDL
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可