ステンレス鋼における低サイクル疲労き裂発生の超音波顕微鏡による観察

• 荒居 善雄

  埼玉大学工学部

• 土田 栄一郎

  埼玉大学工学部

• 直見 英明

  埼玉大学大学院

書誌事項

タイトル別名

• Observation of Low CycleFatigue Crack Initiation in Stainless Steel using Scanning Acoustic Microscope
• ステンレス コウ ニ オケル テイサイクル ヒロウ キレツ ハッセイ ノ チョウオンパ ケンビキョウ ニ ヨル カンサツ

抄録

The objective of present study is to develop a prediction method of residual fatigue life of cyclically loaded metallic materials in early stage of its life. A change in intensity of ultrasonic back reflection wave from the material surface under cyclic loading was measured. The relation of the change to a fatigue damage of the material was examined through the microscopic surface observations using optical microscope and atomic-force microscope. An increase of the ultrasonic back reflection intensity occurs due to the fatigue crack initiation at the slip band. This technique enable one to detect the initiation of fatigue damage at a number of cycles before the 85% of the fatigue crack initiation life until the crack length being 0.1mm.

収録刊行物

• 実験力学

  実験力学 4 (4), 297-303, 2004

  日本実験力学会

キーワード

• Ultrasonic Method
• Scanning Acoustic Microscope
• Fatigue Crack
• Crack Initiation Life
• Low Cycle Fatigue

詳細情報

• CRID: 1390001205188531968
• NII論文ID: 10014193396
• NII書誌ID: AA11822914
• DOI: 10.11395/jjsem2001.4.297
• ISSN: 18844219
• ISSN: 13464930
• NDL書誌ID: 7196794
• Web Site: http://id.ndl.go.jp/bib/7196794
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I7196794
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • CiNii Articles
  • KAKEN
• 抄録ライセンスフラグ: 使用不可