Electrochemical Reduction of Titanium Tetrabromide in a Hydrophobic Room-temperature Molten Salt
-
- KATAYAMA Yasushi
- Department of Applied Chemistry, Faculty of Science and Technology, Keio University
-
- OGAWA Koichi
- Department of Applied Chemistry, Faculty of Science and Technology, Keio University
-
- MIURA Takashi
- Department of Applied Chemistry, Faculty of Science and Technology, Keio University
この論文をさがす
抄録
<p>The electrochemical reduction of tetravalent titanium species was investigated in hydrophobic 1-n-butyl-1-methylpyrrolidinium bis(trifluoromethylsulfonyl)imide (BMPTFSI) room-temperature molten salt (ionic liquid). Titanium tetrabromide was soluble in BMPTFSI regardless of the presence of BMPBr as a Lewis base. The stepwise reduction from Ti(IV) to Ti(III) and probably Ti(II) was observed in BMPTFSI containing TiBr4 without BMPBr. The potentiostatic cathodic reduction gave some deposits at 180°C. The reduction of Ti(IV) species at −2.3 V led to the deposition of some Ti compounds containing TFSI− anions. The electrodeposit containing Ti without TFSI− anions was obtained by the potentiostatic cathodic reduction below −3.0 V.</p>
収録刊行物
-
- Electrochemistry
-
Electrochemistry 73 (8), 576-578, 2005-08-05
公益社団法人 電気化学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001288142091392
-
- NII論文ID
- 10015418588
-
- NII書誌ID
- AN00151637
-
- ISSN
- 21862451
- 13443542
-
- NDL書誌ID
- 7444962
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用可