Au Alloy Formation with Sn-Pb or Sn-Zn Solder Nanoparticles

• Shintaku Masayuki

  Department of Nanophysics in Frontier Project, Ritsumeikan University

• Suzuki Hitoshi

  Department of Nanophysics in Frontier Project, Ritsumeikan University

• Kamitsuji Katsuya

  Department of Nanophysics in Frontier Project, Ritsumeikan University

• Kaito Chihiro

  Department of Nanophysics in Frontier Project, Ritsumeikan University

抄録

Structures of simultaneously evaporated Sn–Pb and Sn–Zn nanoparticles on amorphous carbon surfaces have been elucidated using a transmission electron microscope. Spontaneous alloy formations by the deposition of Au have been observed at room temperature on a clean particle surface. AuSn₂, Au₃Zn and AuPb₂ ordered alloys have predominantly been produced. It was also shown that the spontaneous formation of oxide film with the thickness of 5.0 nm order upon exposure to air prevents the alloy formation even with heating at 300°C.

収録刊行物

• Japanese Journal of Applied Physics

  Japanese Journal of Applied Physics 44 (7A), 5296-5299, 2005

  The Japan Society of Applied Physics

キーワード

• transmission electron microscope
• alloying
• ordered phase
• solder

詳細情報

• CRID: 1390001206266708608
• NII論文ID: 10016610137
• NII論文ID: 210000058423
• NII論文ID: 130004534402
• NII書誌ID: AA10457675
• DOI: 10.1143/jjap.44.5296
• ISSN: 13474065
• ISSN: 00214922
• NDL書誌ID: 7363219
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I7363219
• Web Site: https://iopscience.iop.org/article/10.1143/JJAP.44.5296
• Web Site: https://iopscience.iop.org/article/10.1143/JJAP.44.5296/pdf
• 本文言語コード: en
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可