Ce–Cu–Fe–Al–Si Bulk Metallic Glass Alloys With High Glass Forming Ability
-
- Bian Zan
- Institute for Materials Research, Tohoku University
-
- Inoue Akihisa
- Institute for Materials Research, Tohoku University
書誌事項
- タイトル別名
-
- Ce–Cu–Fe–Al–Si Bulk Metallic Glass Alloys With High Glass Forming Ability
この論文をさがす
抄録
New Ce–Cu–Fe–Al–Si bulk metallic glasses (BMGs) with high glass formation ability (GFA) and large supercooled liquid regions (ΔTx, ΔTx=Tx–Tg) were developed. Investigation shows that the addition of Fe and Si elements is very effective to improve the glass formation ability of Ce-based BMGs. For an optimizing composition, the ΔTx value is 95 K and the alloy can be prepared into bulk metallic glass rods with the diameters of at least 10 mm. In the Ce–Cu–Al–Fe alloys, the glass transition temperature (Tg), crystallization temperature (Tx) and ΔTx increase with increasing Fe content. The reduced glass transition temperature (Trg=Tg⁄Tl) of the present BMG system is about 0.5–0.6 and is much lower than that of other metal base BMG systems with high GFA. Compressive fracture strength (σf) and Young’s modulus (E) of the Ce–Cu–Al–Fe BMGs are ∼930 MPa and ∼45 GPa, respectively, and increase with increasing Fe content.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 46 (11), 2541-2544, 2005
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204249966592
-
- NII論文ID
- 130004452666
- 10016869376
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 7710826
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可