Mechanical Properties of Thermomechanical Treated Hyper-Eutectic Al–Si–(Fe,Mn,Cu) Materials
-
- Umezawa Osamu
- Division of Mechanical Engineering and Materials Science Graduate School of Engineering, Yokohama National University
書誌事項
- タイトル別名
-
- Mechanical Properties of Thermomechanical Treated Hyper-Eutectic Al–Si–(Fe,Mn,Cu) Materials
この論文をさがす
抄録
Tensile and high-cycle fatigue behavior of thermomechanical treated hyper-eutectic Al–Si–(Fe,Mn,Cu) materials were studied. Through the repeated thermomechanical treatment (RTMT) which is a repeat of the multi steps cold-working followed by heat treatment, Si crystals and/or intermetallic compounds were broken into some fragments and dispersed in the aluminum matrix. Fine dispersion of the second phase particles exhibited good ductility, since early fracture was overcome. A few large Si crystals or aggregates of compounds, however, gave an origin of fatigue crack generation. Since microcrack linkage generates a larger fetal crack, not only refinement but also random distribution of second particles may be required to improve fatigue strength at and below room temperature. At higher temperature, on the other hand, dynamic recovery may cause apparent strain rate dependence on flow curves.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 46 (12), 2616-2623, 2005
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204250205312
-
- NII論文ID
- 130004452679
- 10017149293
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD28Xht1Ohur0%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 7757403
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- IRDB
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可