Relaxation and Crystallization Behavior of the Zr50Cu40Al10 Metallic Glass
-
- Yano Takaaki
- Department of Materials Science, Osaka Prefecture University
-
- Yorikado Yuhi
- Department of Materials Science, Osaka Prefecture University
-
- Akeno Yasutake
- Graduate School of Engineering, University of Hyogo
-
- Hori Fuminobu
- Department of Materials Science, Osaka Prefecture University
-
- Yokoyama Yoshihiko
- Institute for Materials Research, Tohoku University
-
- Iwase Akihiro
- Department of Materials Science, Osaka Prefecture University
-
- Inoue Akihisa
- Institute for Materials Research, Tohoku University
-
- Konno Toyohiko J.
- Department of Materials Science, Osaka Prefecture University
書誌事項
- タイトル別名
-
- Relaxation and Crystallization Behavior of the Zr<SUB>50</SUB>Cu<SUB>40</SUB>Al<SUB>10</SUB> Metallic Glass
この論文をさがす
抄録
We examined relaxation and crystallization behavior of the ternary Zr50Cu40Al10 metallic glass by using positron annihilation and transmission electron microscopy (TEM). Observed changes in positron annihilation lifetime of the alloy annealed isothermally at 673 K, which is below the glass transition temperature, correlate well with observed density changes; while coincidence Doppler broadening (CDB) spectra exhibit no significant change. These observations demonstrate that free volume decreases without a rearrangement of atoms during structural relaxation. On the other hand, CDB spectrum has exhibited considerable changes when the same alloy was annealed at 773 K. TEM observations suggested that crystallization occurs via growth of spherulites of several hundred nm in diameter, which themselves are composed of radially grown grains. Chemical analysis revealed that Cu atoms are partitioned out during the growth of the spherulites. Diffraction study indicated that the unit cell of the crystalline phase belong to an orthorhombic system with a=0.892, b=0.550, and c=1.060 nm; while remaining inter-spherulite regions are found to crystallize into an fcc phase with a=1.28 nm, which is probably isostructural to the τ3 phase.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 46 (12), 2886-2892, 2005
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204250483712
-
- NII論文ID
- 130004452726
- 10017150197
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 7757976
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可