Crack Nucleation Mechanism of Austempered Ductile Iron during Tensile Deformation
-
- Yajima Zenjiro
- Advanced Materials Science Research and Development Center, Kanazawa Institute of Technology
-
- Kishi Yoichi
- Advanced Materials Science Research and Development Center, Kanazawa Institute of Technology
-
- Shimizu Ken’ichi
- Advanced Materials Science Research and Development Center, Kanazawa Institute of Technology
-
- Mochizuki Hideharu
- Sugiyama Co., Ltd.
-
- Yoshida Toshiki
- Industrial Property Cooperation Center
この論文をさがす
抄録
The relationship between the crack nucleation and stress-induced martensitic transformation in the retained massive austenites (RM-γ’s) of austempered ductile irons (ADIs) was examined in detail by carrying out tensile tests and scanning electron microscope (SEM) observations for an ADI material. The SEM observations revealed that cracks were not nucleated in the peripheral regions of graphite nodules but were nucleated in the RM-γ’s. Surface relief due to stress-induced martensitic transformation was observed near the cracks in the RM-γ’s, and it was also observed in the RM-γ’s in which cracks were not visible. For this reason, the cracks were concluded to be nucleated mainly in the RM-γ’s subjected to stress-induced martensitic transformation.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 47 (1), 82-89, 2006
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679227352448
-
- NII論文ID
- 130004452940
- 10017151260
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 7772949
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可