Crystal Alignment of Sn-Pb Alloy by Controlled Imposition of a Static Magnetic Field and an Alternating Electric Current during Solidification
-
- Usui Manabu
- Graduate Student of Nagoya University
-
- Iwai Kazuhiko
- Department of Materials, Physics and Energy Engineering, Graduate School of Engineering, Nagoya University
-
- Asai Shigeo
- Department of Materials, Physics and Energy Engineering, Graduate School of Engineering, Nagoya University
この論文をさがす
抄録
In this study, a new process for a crystal alignment of an alloy during solidification has been proposed in which the imposing periods of a static magnetic field and an alternating current are controlled. In the initial stage of the solidification both the magnetic and electric fields are imposed on the alloy to break dendrites into pieces and to spread them to the whole area of the sample. In the next stage, only the static magnetic field was applied for the sample. The function of the static magnetic field in this stage is not only the rotation of the crystals to magnetically stable direction but also the suppression of the disturbance such as liquid motion. The principle of this process was experimentally confirmed by using a Sn–10mass%Pb alloy. In the X-ray diffraction pattern of the sample solidified without the static magnetic field, the first and second highest peaks were (101)-plane and (200)-plane. That is, the crystal direction is random. On the other hand, only the peaks corresponding to a,b-plane were observed in the sample solidified under the imposition of the controlled electromagnetic field. Therefore, this process is useful for the crystal alignment of alloy.
収録刊行物
-
- ISIJ International
-
ISIJ International 46 (6), 859-863, 2006
一般社団法人 日本鉄鋼協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206487225472
-
- NII論文ID
- 10018047094
-
- NII書誌ID
- AA10680712
-
- COI
- 1:CAS:528:DC%2BD28XmtlOlsb0%3D
-
- ISSN
- 13475460
- 09151559
- http://id.crossref.org/issn/00211583
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可