- Tensile and Fatigue Strengths of SCS-6/Ti-6Al-4V Titanium Matrix Composite by Spark Plasma Sintering
- 放電プラズマ焼結法によるSCS-6/Ti-6Al-4V複合材料の引張および疲労強度
- ホウデン プラズマ ショウケツホウ ニ ヨル SCS 6 Ti 6Al 4V フクゴウ ザイリョウ ノ ヒッパリ オヨビ ヒロウ キョウド
この論文をさがす
抄録
This study was undertaken to investigate the effect of spark plasma sintering (SPS) on the tensile and fatigue properties of laminates of SCS-6 SiC fiber-reinforced Ti-6Al-4V titanium matrix composites (TMC). The Ti-6Al-4V matrix and SCS-6 fiber mat were consolidated by spark plasma sintering at the temperature of 800, 900, and 1000°C and at the pressures of 30 and 60 MPa in vacuum. Tensile specimens of TMC were tested at room temperature, 400, 600, and 800°C. In addition, tensile properties of TMC were experimentally evaluated with 11 to 33% volume fraction of SCS-6. Fatigue tests of TMC were carried out at room temperature and 600°C. Specimens were examined after tensile and fatigue tests using SEM to characterize the fracture surface morphology. The fiber/matrix interactions were analyzed by energy dispersive x-ray spectroscopy (EDS).<br>TMC consolidated at 900°C and 60 MPa showed the highest strengths of 857 to 1679 MPa from room temperature to 800°C. The tensile strengths of TMC with volume fraction of fiber varied from 11 to 27% are approximately equal to the theoretical obtained from the rule-of-mixture model. TMC can sustain tensile stress level at or below 450 MPa at 600°C without fracture after more than 107 cycles.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 52 (10), 722-729, 2005
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681283996160
-
- NII論文ID
- 10018283413
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 7709707
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可