Precipitation Processes in a Cu–0.9 mass% Be Single Crystal
-
- Monzen Ryoichi
- Division of Innovative Technology and Science, Kanazawa University
-
- Watanabe Chihiro
- Division of Innovative Technology and Science, Kanazawa University
書誌事項
- タイトル別名
-
- Precipitation Processes in a Cu–0.9 mass% Be Single Crystal
- Precipitation Processes in a Cu 0 9 massパーセント Be Single Crystal
この論文をさがす
抄録
The precipitation processes in a Cu–0.9 mass%Be alloy single crystal containing only G.P. zones parallel to the matrix (001)α plane have been studied by high-resolution transmission electron microscopy. The precipitation sequence found is: G.P. zones→γ″→γ′I→γI+γ′→γ. The γ″ phase has a two-layer structure of Be atoms separated by a matrix layer parallel to (001)α, and a body-centered tetragonal (bct) lattice. The γ′I phase consisting of five to ten Be-layers is body-centered monoclinic. The γI phase continuously transforms from the G.P. zones via γ″ and γ′I. The heterogeneous formation of γ′ occurs on the γI phase. The γI or γ′ phase is bct with a=b=0.254 nm and c=0.352 nm or a=0.254 nm and b=c=0.268 nm. The γ″, γ′I or γI phase aligns with the matrix according to the Bain orientation relationship. The plate-shaped γ′ precipitates have the (1\\bar1\\bar2)α habit plane and the orientation relationship, (1\\bar1\\bar2)α||(0\\bar1\\bar2)γ′; [110]α||[100]γ′ (OR I), or the (1\\bar13)α habit plane and the orientation relationship, (1\\bar13)α||(0\\bar13)γ′; [110]α||[100]γ′ (OR II). The structure of γ′ successively changes into that of the γ phase with a=0.280 nm for OR I or 0.268 nm for OR II. The γ precipitates of OR I and OR II are elongated along approximately [1\\bar11]α and [3\\bar3\\bar2]α, which are in good agreement with the invariant-line directions.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 47 (12), 2925-2934, 2006
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679227014528
-
- NII論文ID
- 130004452995
- 10018421366
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD2sXit1Wiurg%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 8587815
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可