The Formation and Characterization of Nanocrystalline Phases by Mechanical Milling of Biphasic Calcium Phosphate/Poly-L-Lactide Biocomposite
-
- Nikcevic I.
- Institute of Technical Sciences of the Serbian Academy of Sciences and Arts
-
- Maravic D.
- The Vinca Institute of Nuclear Sciences
-
- Ignjatovic N.
- Institute of Technical Sciences of the Serbian Academy of Sciences and Arts
-
- Mitric M.
- The Vinca Institute of Nuclear Sciences
-
- Makovec D.
- Jo\\v{z}ef Stefan Institute
-
- Uskokovic D.
- Institute of Technical Sciences of the Serbian Academy of Sciences and Arts
書誌事項
- タイトル別名
-
- Formation and Characterization of Nanocrystalline Phases by Mechanical Milling of Biphasic Calcium Phosphate Poly L Lactide Biocomposite
この論文をさがす
抄録
Biphasic calcium phosphate/poly-L-lactide granules of 150–200 μm sizes were subjected to high-energy mechanical milling in a planetary ball mill for up to 480 minutes. Characterization of the material obtained was carried out using X-ray diffraction (XRD), differential scanning calorimetry (DSC), environmentally scanning electronic microscopy (ESEM), transmission electron microscopy (TEM) and infrared spectroscopy (IR). These techniques confirmed that mechanical milling induced significant changes in the biocomposite structure and properties. The most significant changes are reduction of the HAp crystallites size from 99.8 to 26.7 nm and β-TCP from 97.3 to 29.6, as well as crystallinity of PLLA phases. Homogeneous phase distribution (arrangement) is obtained by extending the duration of mechanical milling.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 47 (12), 2980-2986, 2006
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204250313344
-
- NII論文ID
- 130004453002
- 10018421519
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 8587920
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可