Preparation of Fe–Pt–Si Amorphous Ribbons and Their Coercivity after Crystallization
-
- Yamamoto Tokujiro
- Advanced Research Center of Metallic Glasses, Institute for Materials Research, Tohoku University
-
- Omori Akihiro
- Advanced Research Center of Metallic Glasses, Institute for Materials Research, Tohoku University
-
- Makino Akihiro
- Advanced Research Center of Metallic Glasses, Institute for Materials Research, Tohoku University
-
- Inoue Akihisa
- Advanced Research Center of Metallic Glasses, Institute for Materials Research, Tohoku University
Bibliographic Information
- Other Title
-
- Preparation of Fe–Pt–Si Amorphous Ribbons and Their Coercivity after Crystallization
Search this article
Abstract
FexPtySiz (x=60–90, y=10–70, z=10–40) ribbons were prepared using a melt-spinning technique. Fully amorphous ribbons were obtained for alloys containing approximately 20–30 at%Si. Crystallization of the amorphous ribbons yielded composite structures of L10 FePt and Pt–Si intermetallic compounds for Fe45Pt35Si20 and Fe47Pt28Si25. Fe45Pt35Si20 amorphous ribbons were annealed at 700 K for 180 min, producing a grain size of approximately 40 nm in diameter, and a maximum coercivity of 160 kA/m.
Journal
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 48 (1), 74-79, 2007
The Japan Institute of Metals and Materials
- Tweet
Details 詳細情報について
-
- CRID
- 1390282679226183296
-
- NII Article ID
- 130004453342
- 10018666144
-
- NII Book ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL BIB ID
- 8597341
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- Abstract License Flag
- Disallowed