Phase Stability of an Amorphous Phase Against Electron Irradiation Induced Crystallization in Fe-Based Metallic Glasses
-
- Nagase Takeshi
- Division of Materials and Manufacturing Science, Graduate School of Engineering, Osaka University
-
- Nino Akihiro
- Department of Materials Science and Engineering, Graduate School of Engineering, Osaka University
-
- Umakoshi Yukichi
- Division of Materials and Manufacturing Science, Graduate School of Engineering, Osaka University
この論文をさがす
抄録
Electron irradiation induced nano-crystallization of melt-spun amorphous phase in Fe-Zr-B ternary alloys was investigated focusing on the difference in phase stability of amorphous phase during thermal annealing and electron irradiation. Nano-composite structure composed of nano-crystalline α-Fe precipitates with b.c.c.-structure, metallic compounds and a residual amorphous matrix was formed under 2.0 MeV electron irradiation at 298 K, while such nano-structure was hardly realized by thermal annealing. The phase stability of an amorphous phase against electron irradiation was discussed based on the relationship between thermal properties and critical onset total dose of electron irradiation induced crystallization at 298 K.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 48 (6), 1340-1349, 2007
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679227825408
-
- NII論文ID
- 10019486485
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 8742261
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可