Coarsening Kinetics of Al<SUB>3</SUB>Sc Precipitates in an Al–Mg–Sc Alloy Aged at 573 K
-
- Watanabe Daizen
- Division of Innovative Technology and Science, Kanazawa University
-
- Watanabe Chihiro
- Division of Innovative Technology and Science, Kanazawa University
-
- Monzen Ryoichi
- Division of Innovative Technology and Science, Kanazawa University
Bibliographic Information
- Other Title
-
- Coarsening kinetics of Al3Sc precipitates in an Al-Mg-Sc alloy aged at 573K
- Coarsening Kinetics of Al<SUB>3</SUB>Sc Precipitates in an Al–Mg–Sc Alloy Aged at 573 K
Search this article
Abstract
The coarsening of Al3Sc precipitates in an Al–1 mass%Mg–0.27 mass%Sc alloy aged at 573 K has been examined using a model developed by Kuehmann and Voorhees. The average size of Al3Sc precipitates was evaluated by transmission electron microscopy and electrical resistivity was employed to measure the Sc concentration in the matrix. Kinetic analyses revealed that before the onset of a coarsening stage, there exist mixed stages of nucleation and growth and of growth and coarsening. The coherent Al/Al3Sc interface energy γ is estimated as 0.23 Jm−2 from data on coarsening alone. The transition from a coherent interface to a semi-coherent interface caused no change in γ.
Journal
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 48 (6), 1571-1574, 2007
The Japan Institute of Metals and Materials
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390001204251250048
-
- NII Article ID
- 10019487216
-
- NII Book ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD2sXnvVWqsbw%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL BIB ID
- 8743024
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed