The Effects of Yttrium Element on Microstructure and Mechanical Properties of Mg-5 mass%Al-3 mass%Ca Based Alloys Fabricated by Gravity Casting and Extrusion Process
-
- Son Hyeon-Taek
- Korea Institute of Industrial Technology
-
- Lee Jae-Seol
- Korea Institute of Industrial Technology
-
- Kang Chang-Seog
- Korea Institute of Industrial Technology
-
- Bae Jung-Chan
- Korea Institute of Industrial Technology
-
- Yoshimi Kyosuke
- Department of Environmental Studies, Graduate School of Environmental Studies, Tohoku University
-
- Maruyama Kouichi
- Department of Environmental Studies, Graduate School of Environmental Studies, Tohoku University
この論文をさがす
抄録
The as-cast microstructure of Mg-5Al-3Ca-xY alloy consists of dendritic α-Mg matrix, (Mg, Al)2Ca eutectic phase and Al2Y intermetallic compounds. These two kind of (Mg, Al)2Ca compounds were observed: coarse irregular-shape structure at grain boundary and fine needle-shape structure in the α-Mg matrix grain. This (Mg, Al)2Ca phase of the extruded alloys was elongated to extrusion direction and size of this phase was refined comparing with that of as-cast alloys because of severe deformation during hot extrusion. Maximum yield and ultimate strength value of extruded alloys was 326 and 331 MPa at Mg-5Al-3Ca-3Y alloy, respectively. From these results, it is conclusively demonstrated that Y additions on Mg-5Al-3Ca alloy have more effect to improve mechanical properties.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 49 (5), 945-951, 2008
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204249364864
-
- NII論文ID
- 10021146382
- 130004454010
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 9480248
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可