Experimental Determination of Forming Limit Diagram and Springback Characteristics of AZ31B Mg Alloy Sheets at Elevated Temperatures

DOI Web Site Web Site 被引用文献5件 参考文献31件

この論文をさがす

抄録

A warm/hot formability testing apparatus was designed and fabricated for this study. The forming limit curve (FLC) and springback characteristics of AZ31B Mg alloy sheets at elevated temperatures of up to 300°C were investigated. The forming limit increased rapidly with temperature up to 200°C, and increased slightly thereafter. In the range from 200 to 300°C, the FLC0 was found to be six to seven times higher than at room temperature. In isothermal springback tests, the effect of the blank holding force (BHF) on springback differed slightly from that for other metal sheets at low temperatures. At 200°C and above, negligible springback was observed over the range of BHF’s used. With increasing temperatures, springback decreased rapidly up to 200°C, and very slowly afterward. In nonisothermal tests, considerable springback was observed, even at temperatures of 200°C or higher; furthermore, it decreased almost linearly with increases in both the temperature and BHF.

収録刊行物

被引用文献 (5)*注記

もっと見る

参考文献 (31)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ