すべり摩擦を受けた（００１）銅単結晶における結晶の回転と小角粒界の形成

DOI Web Site Web Site 被引用文献4件 参考文献28件

書誌事項

タイトル別名
  • Lattice Rotation and Formation of Low-Angle Boundary in a (001) Copper Single Crystal Subjected to Sliding Wear
  • スベリ マサツ オ ウケタ 001 ドウ タンケッショウ ニ オケル ケッショウ ノ カイテン ト ショウカク リュウカイ ノ ケイセイ

この論文をさがす

抄録

  A sliding wear test was conducted on a copper single crystal having (001) surface. Formation of fine grains was recognized locally near the worn surface. To find a criterion for generation of low-angle boundaries during the sliding wear, lattice rotation of the matrix and misorientation between adjoining points were measured using electron backscatter diffraction (EBSD) analysis. Particularly, we paid attention to the low-angle boundaries that were distant from the worn surface. Beneath the fine-grained area, orientation of the matrix continuously changed along the direction of depth. The continuous lattice rotation was understood from a concept of geometrically necessary (GN) dislocations whose density is proportional to a lattice rotation gradient ∂φ/∂x. Increase in the lattice rotation gradient that was measured from the EBSD analysis was recognized near the worn surface. However, at the subsurface layer where low-angle boundaries were generated, the lattice rotation gradient was no longer a function of depth, and was smaller than that of the region where the continuous lattice rotation occurred. Accordingly, the generation of the low-angle boundary could be caused by rearrangement of the dislocations that was induced by the sliding wear.<br>

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 72 (8), 625-630, 2008

    公益社団法人 日本金属学会

被引用文献 (4)*注記

もっと見る

参考文献 (28)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ