- Fabrication of Mg-Fe-O Ferrite/magnetic Metal Bulk Composites by High-pressure Sintering
- 高圧焼結法によるMg-Fe-O酸化物フェライト/磁性金属系複合材料の作製
- コウアツ ショウケツホウ ニ ヨル Mg Fe O サンカブツ フェライト ジセイ キンゾクケイ フクゴウ ザイリョウ ノ サクセイ
この論文をさがす
抄録
Fabrication of MgFe2O4/Fe-Ni alloy bulk composites, in which Fe-Ni grains (∼5 μm in diameter) are fully surrounded with thin MgFe2O4 layer (∼0.3 μm in thick), has been tried by adopting high-pressure sintering for two powders: "Composite Powder I" and "Composite Powder II". The former was prepared as follows; fine MgO particle-coated Fe-Ni powders were heat-treated under various oxygen partial pressures at 600° and 700°C. The latter was fine MgO+α-Fe2O3 mixed powder particles-coated Fe-Ni powders. For the composite powders, two sintering processes were tried; i.e., pulsed-electric current pressure sintering PECPS (800°C/30 MPa/3 min) and HIP (950°-1250°C/196 MPa/2 h). Phase identification by XRD and SEM observations revealed that dense microstructure consisting of two phases (spinel MgFe2O4 and Fe-Ni alloy) was attained from the combination of composite powders II, PECPS and a re-oxidation process. However, other process resulted in formation of Wüsteit phase of Mg1-xFexO and FeO in addition to Fe-Ni due to highly reductive atmosphere during the sintering. Thus obtained composite materials consisting two phases showed good magnetic properties at room temperature as expected from their compositions and microstructures: saturation magnetization density Bs of 1.20 T, and permeability μ∼15-30 at 1 MHz, and a Curie point above 460°C.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 55 (9), 629-636, 2008
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681285696256
-
- NII論文ID
- 10024350841
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DC%2BD1cXhtFKru7rM
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 9660468
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可