Synthesis of Manganese Ferrite by Microwave Discharge between Carbon Felts (MD/CF) at Ambient Pressure
-
- Kurihara Hideki
- Saitama Industrial Technology Center
-
- Yajima Tatsuhiko
- Faculty of Engineering, Saitama Institute of Technology
-
- Nomura Kiyoshi
- School of Engineering, The University of Tokyo
この論文をさがす
抄録
Manganese ferrites were quickly prepared from manganese oxide and iron oxide powders by a microwave discharge generated between two pieces of carbon felt (MD/CF) with various powers in air atmosphere, and were characterized especially by X-ray diffractometry and Mössbauer spectroscopy. MnFe2O4 was produced within at least 40 s by MD/CF with more than 200 W microwave power in air atmosphere. With the increase of the applied microwave power, FeO powders were produced in addition to distorted MnFe2O4 by using MnO and Fe2O3 powders as starting mixture. Improved yield for MnFe2O4 were obtained by post annealing for 1 hour or by using the raw mixed materials of MnO, MnO2 and Fe2O3.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 56 (3), 116-120, 2009
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206308631040
-
- NII論文ID
- 10025398287
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DC%2BD1MXjsl2mt70%3D
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 10237346
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可