Detection of Hydrogen Evolution during Tensile Deformation and Fracture in Carbon Steel
-
- Horikawa Keitaro
- Department of Mechanical Science and Bioengineering, School of Engineering Science, Osaka University
-
- Okada Hiroaki
- Department of Mechanical Science and Bioengineering, School of Engineering Science, Osaka University
-
- Kobayashi Hidetoshi
- Department of Mechanical Science and Bioengineering, School of Engineering Science, Osaka University
-
- Urushihara Wataru
- Surface Design & Corrosion Research Section, Materials Research Laboratory, Kobe Steel, Ltd.
Search this article
Abstract
Hydrogen evolution behavior during tensile deformation and fracture in hydrogen-charged and uncharged carbon steels was investigated using a hydrogen microprint technique (HMT). A tensile testing machine equipped with a mass spectrometer placed in an ultrahigh vacuum (UHV) chamber was used to detect hydrogen evolution during the tensile test. In the uncharged specimens, the HMT revealed that silver particles, which represented the emission sites of hydrogen, were clearly observed when the applied strain increased. The accumulation of the silver particles along the slip lines was observed at the surface of the highly deformed specimens adjacent to the fracture zone. This indicated that hydrogen atoms primarily dissolved in the specimen were transported by mobile dislocations. In the hydrogen-charged specimen, a large number of silver particles were distributed almost uniformly in the matrix even in the undeformed state; however, the preferential distribution of the silver particles on the slip lines was not clearly identified, probably due to the low fracture strain, which resulted from the hydrogen embrittlement. In all the specimens, HMT showed that silver particles were not visible directly on the Al2O3 inclusions after the deformation. Mass spectrometry analysis in the UHV tensile test revealed that evolution of hydrogen gas increased significantly when the specimens were strained to a level that corresponded to maximum stress.
Journal
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 50 (11), 2532-2540, 2009
The Japan Institute of Metals and Materials
- Tweet
Details 詳細情報について
-
- CRID
- 1390001204249418624
-
- NII Article ID
- 10025558862
- 130004454137
-
- NII Book ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BC3cXntlOg
-
- ISSN
- 13475320
- 13459678
-
- NDL BIB ID
- 10417430
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed