Influence of Deaerated Condition on the Corrosion Behavior of AZ31 Magnesium Alloy in Dilute NaCl Solutions

DOI Web Site Web Site 参考文献40件
  • Wang Lei
    Materials Reliability Center, National Institute for Materials Science School of Materials Science and Engineering, University of Science and Technology Beijing
  • Shinohara Tadashi
    Materials Reliability Center, National Institute for Materials Science
  • Zhang Bo-Ping
    School of Materials Science and Engineering, University of Science and Technology Beijing

この論文をさがす

抄録

The corrosion behavior of AZ31 Mg alloy in the nondeaerated and deaerated dilute NaCl solutions was investigated by electrochemical measurements. The cathodic reaction of AZ31 Mg alloy depends on the hydrogen evolution and the oxygen reduction in nondeaerated media, while that is dominanted by the hydrogen evolution in deaerated media. In the potentiostatic measurements in deaerated media, the current density reached a peak during the initial immersion and then showed a stepwise decrease getting into the passivation state by a homogeneous distribution of the Mg(OH)2 product with increasing polarization time. It revealed that AZ31 alloy has a better corrosion resistance in deaerated media after long immersion. In the 0.01 mol/L solution, passivation zone was observed in deaerated media polarization up to −1.35 V (vs. SCE) while the corrosion and passivation zones were occurred in nondeaerated media. Potentiodynamic measurements in the 0.01 mol/L NaCl solution containing various concentrations NaHCO3 showed that the corrosion behavior of AZ31 alloy depends on the NaHCO3 concentration. It means that the presence of CO2 naturally in nondeaerated media may affect the corrosion process.

収録刊行物

  • MATERIALS TRANSACTIONS

    MATERIALS TRANSACTIONS 50 (11), 2563-2569, 2009

    公益社団法人 日本金属学会

参考文献 (40)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ