Synthesis of porous Al3Ti/Al composite and effect of precursor processing condition on cell morphology
-
- Inoguchi Norio
- Department of Materials Science and Engineering, Nagoya University
-
- Kobashi Makoto
- Department of Materials Science and Engineering, Nagoya University
-
- Kanetake Naoyuki
- Department of Materials Science and Engineering, Nagoya University
書誌事項
- タイトル別名
-
- Synthesis of Porous Al<SUB>3</SUB>Ti/Al Composite and Effect of Precursor Processing Condition on Cell Morphology
この論文をさがす
抄録
Porous Al3Ti/Al composite was fabricated by a combustion foaming process, which makes use of exothermic reactions between titanium, aluminum and boron carbide powders. Boron carbide powder was used as an exothermic agent to increase the heat of reaction. Fundamental combustion foaming behavior and effects of processing parameters (Al/Ti blending ratio, addition of exothermic agent and powder compacting pressure) on the foaming behavior were investigated. Combustion foaming took place over temperature ranges between melting points of aluminum and Al3Ti. Exothermic agent addition turned out to be effective to increase the porosity of porous Al3Ti/Al composite. Relative density of the precursor was an important factor, which needed to be higher than a threshold level (0.67) to prevent extremely inhomogeneous pore morphology. By conducting hot extrusion to the precursor, both pore size and porosity were increased. As a result of compressive test, high plateau stress and absorbed energy were achieved by increasing Al/Ti mole blending ratio from 4.0 to 7.0.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 50 (11), 2609-2614, 2009
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679227949824
-
- NII論文ID
- 10025559070
- 130004454126
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 10417791
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可