Influence of Annealing Technology on Drawing Properties of Cold Sheets Rolled with Compact Strip Production Hot Bands
-
- Xu Guang
- Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology
-
- Yang Yi
- Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology
-
- Zhang Xinqiang
- Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology
-
- Zhang Huangqiang
- Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology
Search this article
Abstract
The drawing properties of cold sheets rolled with CSP hot-bands (CSS) are not so good compared to cold sheets rolled with conventional hot bands (CSC). Therefore, influences of annealing technology on drawing properties of CSS have been studied in the paper. Research works included (1) drawing properties of cold sheets rolled with different CSP hot-bands, (2) drawing properties of CSS and CSS, and (3) influences of annealing technology on drawing properties of CSS. The results of annealing experiments, microstructural examinations and drawing property tests have shown that the drawing properties of CSS at higher finish deformation temperature (FDT) and lower coiling temperature (CT) are superior to those of CSS at lower FDT and higher CT. It was also found that the drawing properties of CSC are superior to those of CSS after heat treatment with same annealing technology. The annealing temperature for experimental steel grade (DC03) should be higher than 680°C.
Journal
-
- ISIJ International
-
ISIJ International 47 (12), 1767-1771, 2007
The Iron and Steel Institute of Japan
- Tweet
Details 詳細情報について
-
- CRID
- 1390282681463053056
-
- NII Article ID
- 10027026442
-
- NII Book ID
- AA10680712
-
- ISSN
- 13475460
- 09151559
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed