Refinement of As-cast Austenite Grain in Carbon Steel by Addition of Titanium
-
- Sasaki Masayoshi
- Graduate Student, Hokkaido University
-
- Matsuura Kiyotaka
- Division of Materials Science and Engineering, Graduate School of Engineering, Hokkaido University
-
- Ohsasa Kenichi
- Division of Materials Science and Engineering, Graduate School of Engineering, Hokkaido University
-
- Ohno Munekazu
- Division of Materials Science and Engineering, Graduate School of Engineering, Hokkaido University
この論文をさがす
抄録
Effects of Ti addition on as-cast austenite structure of S45C steel have been investigated by means of furnace cooling experiment at a cooling rate of 0.03°C/s, focusing on the Ti addition ranging from 0 to 0.5 mol%. The Ti addition reduces average austenite grain diameter down to a size comparable to secondary dendrite arm spacing. In samples with the Ti addition, the austenite grain boundary is located at inter-dendritic position where Ti(C,N) particles exist and the refinement of austenite grain structure is ascribable to pinning effect of the Ti(C,N) particle formed in L+γ-Fe+Ti(C,N) phase field. The increment of Ti addition does not substantially change the size of Ti(C,N) particle but increases the number of the Ti(C,N) particles, leading to further refinement of the austenite grains.
収録刊行物
-
- ISIJ International
-
ISIJ International 49 (9), 1362-1366, 2009
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206487571456
-
- NII論文ID
- 10027036642
-
- NII書誌ID
- AA10680712
-
- ISSN
- 13475460
- 09151559
-
- HANDLE
- 2115/75411
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- IRDB
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可