Microstructure Evolution at Severely-deformed Ferrite/Martensite Interfaces in a Layer-integrated Steel
-
- Hayashi Taisuke
- Department of Materials Science & Engineering, The University of Tokyo
-
- Abe Eiji
- Department of Materials Science & Engineering, The University of Tokyo
この論文をさがす
抄録
The microstructure evolution at interfaces of a layer-integrated steel sheet constructed by ferritic (SPCC) and martensitic stainless (SUS420J2) steel layers, which were bonded through a cold-rolling and subsequently annealed at 1000°C, has been investigated using scanning transmission electron microscopy combined with energy dispersive X-ray spectroscopy. We find that microstructures around the SPCC/SUS420J2 interfaces are significantly reconstructed during a short-time annealing at 1000°C followed by quenching into water, and the resultant ferrite/martensite interface is found to be extended into the SPCC side from the original cold-rolled interface. Occurrence of such interface migration can be reasonably explained as due to a martensitic transformation across the composition-gradient interface that is caused by element diffusions during annealing at 1000°C. These microstructural characteristics are discussed by comparing with our recent observations of austenite (SUS304)/martensite (SCM415) interface microstructures (Hayashi et al., ISIJ Int., 49 (2009), 1406), which are formed via the same rolling/annealing procedures, aiming to provide a common aspect on how the strong bonding between the hetero-interfaces can be achieved in the layer-integrated steels.
収録刊行物
-
- ISIJ International
-
ISIJ International 50 (2), 272-278, 2010
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681464978688
-
- NII論文ID
- 10027039368
-
- NII書誌ID
- AA10680712
-
- ISSN
- 13475460
- 09151559
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可