- Fabrication of Iron Hollow Spheres by Reduction Sintering Process
- カンゲン ショウケツホウ ニ ヨル チュウクウテツ ボール ノ サクセイ
この論文をさがす
抄録
Iron hollow spheres were fabricated by reduction sintering process. The reduction of iron oxide completed in a range from 573 to 973 K, and the shrinkage (sintering) advanced rapidly in a range from 673 to 1073 K. In spite of the large shrinkage, the shape of sintered body showed only an at all small distortion from a sphere. The compression curve of the block which joined iron spheres showed the plateau load region where a load change is small, and the average plateau load strongly depends on the compression strength of unit spheres. By means of chemical reaction controlled un-reacted core model, activation energy of reduction process has been estimated to be 22 kJ/mol.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 58 (2), 134-138, 2011
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206312073600
-
- NII論文ID
- 10027916301
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DC%2BC3MXjtFWrtbg%3D
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 11014031
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可