高速回転遊星型ボールミルを用いた短時間プロセスでのＦｅ－４８ａｔ％Ｃｒ合金の合成

• 森下 翔

  （独）産業技術総合研究所

• 中山 博行

  （独）産業技術総合研究所

• 尾崎 公洋

  （独）産業技術総合研究所

• 小林 慶三

  （独）産業技術総合研究所

書誌事項

タイトル別名

• Synthesis of Fe-48at%Cr Alloy by a Short-time Process using Fast-rotating Planetary Ball Milling
• コウソク カイテン ユウセイガタ ボールミル オ モチイタ タンジカン プロセス デ ノ Fe 48at% Cr ゴウキン ノ ゴウセイ

抄録

Fe-48at%Cr powder was synthesized by mechanical alloying (MA) of Fe powder and Cr powder using rapid-rotation type planetary ball mill. Homogeneous MA powder was obtained for only 600 s milling at 900 rpm of orbital speed while it had taken for over 360 ks to homogenize them at 200 rpm. The obtained powder had a crystal structure of bcc lattice and contained no brittle phase such as σ phase. The MA powder was sintered by a pulsed current sintering and completely condensed above 1000 K. The sintered Fe-48at%Cr alloy also has no σ phase. Hardness of the sintered body is Hv 380 and there was no crack around the indentation for Vickers hardness.

収録刊行物

• 粉体および粉末冶金

  粉体および粉末冶金 58 (4), 233-236, 2011

  一般社団法人 粉体粉末冶金協会

キーワード

• Fe-48at%Cr
• mechanical alloying
• planetary ball mill
• σ phase
• pulsed current sintering

詳細情報

• CRID: 1390001206312274560
• NII論文ID: 10028125299
• NII書誌ID: AN00222724
• DOI: 10.2497/jjspm.58.233
• COI: 1:CAS:528:DC%2BC3MXmtFGrs7o%3D
• ISSN: 18809014
• ISSN: 05328799
• NDL書誌ID: 11094876
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I11094876
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可