- Fabrication of Magnesium Based Composite Powders with High Hardness and Hard Magnetic Properties by Mechanical Alloying
- メカニカルアロイングホウ ニ ヨル コウコウド コウジセイ オ ユウスル マグネシウムキ フクゴウ フンマツ ノ ソウセイ
この論文をさがす
抄録
In order to fabricate Mg-based composite powders with high hardness and hard magnetic properties, pure magnesium and barium ferrite powders were mechanically alloyed (MAed) using a vibrational ball mill.<BR>Change in Vickers micro-hardness of the pure magnesium powders as a function of the mechanical milling (MM) times obeyed the crystallite size. Change in Vickers micro-hardness of the composite powders as a function of the amount of barium ferrite obeyed the rule of mixture when the MA time was 120 and 240 min.. On the other hands, change in Vickers micro-hardness of the composite powders as a function of the amount of barium ferrite wasn't obeyed the rule of mixture when the MA time was 20 and 60 min.. Magnetization of the composite powders obeyed the amount of the barium ferrite powder, whereas coercive force of the MAed powders decreased due to the refinement of the barium ferrite powder.<BR>Mg-based composite powders with high hardness and hard magnetic properties were successfully produced by mechanical alloying.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 58 (4), 237-242, 2011
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206312275968
-
- NII論文ID
- 10028125309
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DC%2BC3MXmtFGrs7s%3D
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 11094892
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可