Fatigue Property in Ni-Based Bulk Metallic Glass
-
- Fujita Kazutaka
- Department of Mechanical Engineering, Ube National College of Technology
-
- Misumi Kousuke
- Department of Mechanical Engineering, Ube National College of Technology
-
- Zhang Wei
- Institute for Materials Research, Tohoku University
-
- Inoue Akihisa
- Tohoku University
Bibliographic Information
- Other Title
-
- Ni基バルク金属ガラスの疲労特性
- Niキ バルク キンゾク ガラス ノ ヒロウ トクセイ
Search this article
Abstract
Fatigue test was carried out on Ni-based bulk metallic glass (BMG) for which there is still no reports on fatigue strength. Test alloy rods with a diameter of 2 mm were prepared in Ni60Zr20Nb15Al5 at% systems by copper mold casting method. The tensile strength (σB) was 2.9 GPa. The test specimens were machined to hourglass shape type with a minimum diameter of 0.9 mm. The specimens were tested at a stress ratio of 0.1 and a frequency of 10 Hz. The fatigue limit (σW) and fatigue ratio (σW/σB) in the Ni-based BMG showed high values of 1.68 GPa and 0.58, respectively. The tendency that the σW increased with increasing the σB in BMGs was indicated in the Ni-based BMG. In addition, the fatigue fracture toughness in the Ni-based BMG showed a high value of 14 MPa•m1/2.<br>
Journal
-
- Journal of the Japan Institute of Metals and Materials
-
Journal of the Japan Institute of Metals and Materials 75 (9), 474-478, 2011
The Japan Institute of Metals and Materials
- Tweet
Details 詳細情報について
-
- CRID
- 1390282681459798656
-
- NII Article ID
- 10029530664
-
- NII Book ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL BIB ID
- 11229614
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed