- Colloidal Processing of High Performance Silicon Carbide
- コロイドプロセス ニ ヨル コウセイノウ タンカ ケイソ ノ ゴウセイ
この論文をさがす
抄録
The combination of thermodynamics of colloidal suspensions and the DLVO theory succeeded in constructing a colloidal phase diagram in a map of surface potential and solid content of particles of 10-1000 nm diameters. The experimentally-determined packing density agreed with the prediction from the phase diagram. A phase transition from a dispersed suspension to a flocculated suspension during pressure filtration occurred when an applied pressure exceeded a critical value. Based on the colloidal phase transition, new filtration theories were developed for a flocculated suspension. Multi component colloidal suspensions of the 800 nm SiC-30 nm SiC-150 nm Al2O3-Y ions system were heterocoagulated to distribute uniformly the sintering additives (Al2O3 plus Y2O3) around SiC particles. The green compacts were highly densified above 99% theoretical density by hot-pressing at 1950℃ and the sintered SiC provided flexural strengths above 1000 MPa.
収録刊行物
-
- 粉体工学会誌
-
粉体工学会誌 48 (8), 542-551, 2011
一般社団法人 粉体工学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204513494784
-
- NII論文ID
- 10029617274
-
- NII書誌ID
- AN00222757
-
- ISSN
- 18837239
- 03866157
-
- NDL書誌ID
- 11212168
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可