Incorporation of anti-inflammatory agent into calcium hydroxide pulp capping material: An in vitro study of physical and mechanical properties
-
- LOUWAKUL Phumisak
- Dental Biomaterials Science, Graduate School, Chulalongkorn University
-
- LERTCHIRAKARN Veera
- Department of Microbiology, Faculty of Dentistry, Chulalongkorn University
この論文をさがす
抄録
The aims of this study were to investigate the release of fluocinolone acetonide from an experimental pulp capping material containing fluocinolone acetonide (PCFA) and compare some physical and mechanical properties with Dycal®. The PCFA is a hard-setting calcium hydroxide cement composed of 50 mmol/L fluocinolone acetonide. Conditioned media from the setting material was collected for determination of fluocinolone acetonide release by high performance liquid chromatography and pH measurement by pH meter. The setting time, compressive strength, disintegration, and acid soluble arsenic content were measured according to ISO 3107:2004. Dycal® was used as control. Fluocinolone acetonide could release at a range of suitable concentrations from PCFA. The pH, setting time, and acid soluble arsenic content of PCFA were significantly higher than those of Dycal®. The compressive strength and disintegration of PCFA were comparable to control. PCFA may be considered as an alternative in pulp capping of inflamed dental pulp tissue.
収録刊行物
-
- Dental Materials Journal
-
Dental Materials Journal 31 (1), 32-39, 2012
一般社団法人 日本歯科理工学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204715335552
-
- NII論文ID
- 10030128089
-
- NII書誌ID
- AA10443149
-
- ISSN
- 18811361
- 02874547
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可