Enhancement effect of pre-reacted glass on strength of glass-ionomer cement

この論文にアクセスする

この論文をさがす

著者

抄録

In this paper, we report on the enhanced strength of glass ionomer cement (GIC) by using the process of pre acid-base reaction and spray drying in glass preparation. The pre acid-base reaction was induced by prior mixing of the glass powder with poly(alkenoic acid). The weight ratios of glass powder to poly(alkenoic acid) were varied to investigate the extent of the pre acid-base reaction of the glass. The effect of the spray drying process which produced spherical glass particles on cement strength was also studied and discussed. The results show that adding 2%-wt of poly(alkenoic acid) liquid in the pre-reacted step improved cement strength. GICs prepared using a mixture of pre-reacted glass with both spherical and irregular powders at 60:40 by weight exhibited the highest compressive strength at 138.64±7.73 MPa. It was concluded that glass ionomer cements containing pre-reacted glass with mixed glass morphology using both spherical and irregular forms are promising as restorative dental materials with improved mechanical properties and handling characteristics.

収録刊行物

  • Dental materials journal

    Dental materials journal 31(1), 125-130, 2012-01-01

    日本歯科理工学会

参考文献:  32件中 1-32件 を表示

各種コード

  • NII論文ID(NAID)
    10030128500
  • NII書誌ID(NCID)
    AA10443149
  • 本文言語コード
    ENG
  • 資料種別
    ART
  • ISSN
    02874547
  • データ提供元
    CJP書誌  J-STAGE 
ページトップへ