書誌事項
- タイトル別名
-
- Proposal of Guideline for Bonding to Prevention of Hydrogen Embrittlement at Ta/Zr Bond Interface - Hydrogen Embrittlement in SUS304ULC/Ta/Zr Explosive Bonded Joint -
- Proposal of Guideline for Bonding to Prevention of Hydrogen Embrittlement at Ta/Zr Bond Interface
- - Hydrogen Embrittlement in SUS304ULC/Ta/Zr Explosive Bonded Joint -
- -SUS304ULC/Ta/Zr爆発接合継手の水素脆化に関する研究-
この論文をさがす
抄録
The occurrence condition of hydrogen embrittlement cracking at Ta/Zr bond interface was investigated with respect to the hydrogen content and applied stress in order to propose a guideline for the explosive bonding procedure to prevention of hydrogen embrittlement. Hydrogen charging test was conducted for SUS304ULC/Ta/Zr explosive bonded joints applied the different flexural strains. A hydrogen embrittlement crack occurred in the Zr substrate at Ta/Zr bond interface after hydrogen charging, and it was initiated at shorter charging times when the augmented strain was increased. The occurrence condition of hydrogen embrittlement cracking at Ta/Zr bond interface was shifted to lower stress and hydrogen content with an increase in the amount of explosive during bonding. It was suggested that hydrogen embrittlement in Ta/Zr explosive bonded joint could be inhibited by reducing the initial hydrogen content in Ta substrate less than approx. 5ppm.
収録刊行物
-
- 溶接学会論文集
-
溶接学会論文集 28 (2), 248-254, 2010
一般社団法人 溶接学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679703170560
-
- NII論文ID
- 10030150100
-
- NII書誌ID
- AN1005067X
-
- ISSN
- 24348252
- 02884771
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可