ニッケル電鋳に関する条件変化による各反りの最小化検討 Investigation of Minimization of Warp by Varying Conditions on Nickel Electroforming

この論文にアクセスする

この論文をさがす

著者

抄録

Electroforming related to this study was conducted by varying conditions singly, such as the concentration of sodium lauryl sulfate (SLS) in the nickel sulfamate bath, the current density, or the plate thickness. The warp mechanism of electroformed plate was investigated by measuring the internal stress, the orientation using X-ray diffraction, and Vickers hardness. Results show that lowering the current density or the concentration of SLS, or increasing the electroformed plate thickness can minimize warping of the electroformed plate. When SLS was added to the nickel sulfamate bath, the surface tension decreased remarkably up to 0.01 g/dm<sup>3</sup> (threshold, i.e., critical micelle concentration, cmc). Then it decreased only to a slight degree at concentrations higher than 0.01 g/dm<sup>3</sup>. On the other hand, the warp, Vickers hardness, and the orientation index of {220} of the electroformed plates increased remarkably up to 0.01 g/dm<sup>3</sup>. It scarcely increased at concentrations higher than 0.01 g/dm<sup>3</sup>. Therefore, it became apparent that structural changes of crystallites occurred in 0.01 g/dm<sup>3</sup> (cmc) of the concentration of SLS as a border. Based on results of combustion analysis for the electroformed plates, atoms consisting of a single SLS, except the micelle, were incorporated in the crystallites, thereafter affecting various mechanical properties.

収録刊行物

  • 表面技術 = The journal of the Surface Finishing Society of Japan

    表面技術 = The journal of the Surface Finishing Society of Japan 63(2), 118-123, 2012-02-01

    一般社団法人 表面技術協会

参考文献:  25件中 1-25件 を表示

  • <no title>

    WATSON S.

    Tans IMF 67, 89, 1989

    被引用文献1件

  • <no title>

    KAWASAKI W.

    J. Surf. Finish. Soc. Jpn. 34, 15, 1996

    被引用文献1件

  • <no title>

    LEE N.

    Optical Review 10, 290, 2003

    被引用文献1件

  • <no title>

    YASUI M.

    J. Surf. Finish. Soc. Jpn. 52, 734, 2001

    被引用文献1件

  • <no title>

    YASUI M.

    J. Surf. Finish. Soc. Jpn. 55, 226, 2004

    被引用文献1件

  • <no title>

    SAOTOME Y.

    J. Surf. Finish. Soc. Jpn. 55, 248, 2004

    被引用文献1件

  • <no title>

    HUANG C.

    Metal Finishing 91, 107, 1993

    被引用文献1件

  • <no title>

    ABE H.

    J. Surf. Finish. Soc. Jpn. 57, 515, 2006

    被引用文献1件

  • <no title>

    ABE H.

    Material Transactions 48, 2165, 2007

    被引用文献1件

  • <no title>

    WILLSON K. S.

    Tech. Proc. Amer. Electroplaters Soc. 51, 92, 1964

    被引用文献1件

  • <no title>

    小宮山好道

    X線解析 136, 1970

    被引用文献1件

  • <no title>

    BUSH G. W.

    J. Electrochem. Soc. 111, 289, 1964

    被引用文献1件

  • <no title>

    近藤保

    界面化学 75, 1971

    被引用文献1件

  • <no title>

    PANGAROV N. A.

    Electrochim. Acta 7, 139, 1962

    被引用文献1件

  • <no title>

    MARUYAMA Y.

    J. Surf. Finish. Soc. Jpn. 48, 68, 1997

    被引用文献1件

  • <no title>

    ONO T.

    J. Surf. Finish. Soc. Jpn. 58, 482, 2007

    被引用文献1件

  • <no title>

    ARAI S.

    J. Surf. Finish. Soc. Jon. 44, 336, 1993

    被引用文献1件

  • <no title>

    ABE H.

    J. Japan Inst. Metals 68, 844, 2004

    被引用文献1件

  • <no title>

    KISHIMOTO K.

    J. Surf. Finish. Soc. Jpn. 54, 710, 2003

    被引用文献1件

  • <no title>

    TSURU Y.

    J. Surf. Finish. Soc. Jpn. 54, 35, 2003

    被引用文献1件

  • <no title>

    BARRETT R. C.

    Plating 41(9), 1027, 1954

    被引用文献1件

  • <no title>

    BRENNER A.

    Plating 39(8), 865, 1952

    被引用文献1件

  • <no title>

    WEIL R.

    Plating 58(2), 137, 1971

    被引用文献1件

  • <no title>

    WEIL R.

    Plating 58(1), 50, 1971

    被引用文献1件

  • <no title>

    WANG D. D.

    J. Vac. Sci. Technol. A8, 3163, 1990

    DOI 被引用文献3件

各種コード

  • NII論文ID(NAID)
    10030476644
  • NII書誌ID(NCID)
    AN1005202X
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    09151869
  • NDL 記事登録ID
    023510089
  • NDL 請求記号
    Z17-291
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ