Ｍｇ‐Ｌｉ‐Ｙ合金の耐食性に対するアノード酸化処理条件の影響

DOI Web Site 被引用文献2件 参考文献33件

書誌事項

タイトル別名
  • Effect of anodizing condition on corrosion resistance of Mg-Li-Y alloy
  • Mg-Li-Y合金の耐食性に対するアノード酸化処理条件の影響
  • Mg Li Y ゴウキン ノ タイショクセイ ニ タイスル アノード サンカ ショリ ジョウケン ノ エイキョウ

この論文をさがす

抄録

Effects of anodizing conditions on corrosion resistance of Mg–Li–Y alloy, which is most prominent super light alloy capable for easy deformation, were investigated with attention to the formation behavior and microstructure of anodic films. Barrier films or semi-barrier films were formed except at around 7 V and breakdown voltages similar to those associated with typical pure magnesium and AZ alloys. At the former voltages, thick porous type films were formed. The critical voltage of high current flow accompanied by breakdown was dependent on substrate composition; 45 V for Mg–Li–Y alloy, 60 V for 99.95% Mg and 120 V for AZ91D. When aluminate or phosphate ion was added in the electrolyte, the critical voltage of Mg–Li–Y alloy increased to 100 V. Lithium was highly enriched at the outer part of the film and yttrium was enriched in the middle to inner part when the film was barrier type. The ratio of barrier film thickness to anodizing voltage was as high as 4.25 nm/V compared to 1.9 nm/V of that associated with 99.95% Mg. When the film was porous type, the content of both lithium and yttrium decreased and distribution of both elements became uniform. Anodic films formed in sodium phosphate solution followed by sealing treatment in silicate exhibited sufficient corrosion resistance for practical usage.

収録刊行物

  • 軽金属

    軽金属 61 (2), 60-65, 2011

    一般社団法人 軽金属学会

被引用文献 (2)*注記

もっと見る

参考文献 (33)*注記

もっと見る

関連プロジェクト

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ