Effects of P Addition on Corrosion Properties of Soft Magnetic FeSiB Alloys
-
- Dan Zhenhua
- Institute for Materials Research, Tohoku University
-
- Makino Akihiro
- Institute for Materials Research, Tohoku University
-
- Hara Nobuyoshi
- Department of Materials Science, Tohoku University
Search this article
Abstract
Electrochemical behavior of Fe76Si9B15−xPx alloy (x = 0, 2, 5, 7, 10) ribbons in borate buffer solution of pH 8.45 had been investigated. The as-spun ribbons had an amorphous structure. The lower current densities of P-added FeSiBP ribbons with native oxide films were observed at low applied potentials. The minimum P concentration for enhancing the corrosion properties was estimated to be 5 to 7 at%. The current densities of the FeSiBP ribbons after removal of the oxide films were suppressed to lower levels in comparison with that of Fe76Si9B15 ribbons. The formation of a phosphate-containing layer helps passivating the ribbons due to the low solubility of iron phosphate compounds.
Journal
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 54 (9), 1691-1696, 2013
The Japan Institute of Metals and Materials
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282679226386304
-
- NII Article ID
- 10031194657
-
- NII Book ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BC3sXhslejtrnE
-
- ISSN
- 13475320
- 13459678
-
- NDL BIB ID
- 024795274
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- Abstract License Flag
- Disallowed