- Mechanical Properties of TiN-TiAl Composites
Search this article
Abstract
application
TiN-TiAl ceramics/intermetallic composites containing no additives were hot-pressed from a mixture of TiN, Ti and Al powders containing 5 up to 100massl%TiAl (5, 20, 40, 60, 80, 100mass%TiAl), which were formed from a reaction between Ti and Al. Hot-pressing was conducted at 1000℃ for 7.2 ks under a pressure of 13.9 MPa in an Ar gas atmosphere. The mechanical and electrical properties were examined as a function of compositional change from 5 to 100mass%TiAl. TiN-TiAl composites containing 60~100mass%TiAl had a relative density of 67.3~71.1%, bulk density of 2380~2830kg m^<-3>, Vickers hardness of 506~2771MPa, flexural strength of 50~123MPa, Young's modulus of 45.9~82.4GPa, and electrical conductivity of 606~778k S・m^<-1>. The sufficient densification was not necessarily performed because the reaction from Ti and Al to TiAl phase was not completed by the use of coase Ti and Al powders.
Journal
-
- 長野工業高等専門学校紀要
-
長野工業高等専門学校紀要 36 65-71, 2002-06-28
長野工業高等専門学校
- Tweet
Details 詳細情報について
-
- CRID
- 1050001337613938176
-
- NII Article ID
- 110000294259
-
- NII Book ID
- AN00179170
-
- ISSN
- 02861909
-
- NDL BIB ID
- 6223980
-
- Text Lang
- ja
-
- Article Type
- departmental bulletin paper
-
- Data Source
-
- IRDB
- NDL
- CiNii Articles