Ductile-mode High Smoothness Grinding of Fine Ceramics by Diamond Wheel of Coarse Grain Size (2nd Report) - Influence of Wheel Speed on Ductile-mode Grinding of Fine Ceramics -
-
- YASUI Heiji
- 熊本大学工学部
-
- MATSUNAGA Ikuo
- 熊本大学大学院
-
- TSURUSAKI Michiko
- 熊本大学大学院
-
- SAKAMOTO Shigehiko
- 熊本大学工学部
Bibliographic Information
- Other Title
-
- 粗粒ダイヤモンド砥石によるファインセラミックスの延性モード高平滑研削(第2報)―延性モード研削に及ぼす砥石周速度の影響―
- ソリュウ ダイヤモンド トイシ ニ ヨル ファイン セラミックス ノ エンセイ モード コウヘイカツ ケンサク ダイ2ホウ エンセイ モード ケンサク ニ オヨボス トイシシュウ ソクド ノ エイキョウ
- Influence of Wheel Speed on Ductile-mode Grinding of Fine Ceramics
- 延性モード研削に及ぼす砥石周速度の影響
Search this article
Abstract
This report aims to clear the influence of wheel speed on the ductile_mode grinding of hot pressed silicon carbide ceramic with the metal bond diamond wheel of mesh #140 grain size. The experiments are executed by plunge grinding method with surface grinder. The wheel speeds used are 20, 50 and 85m/s. The ground workpiece surface is observed with a differencial interference microscope and SEM, and its roughness is measured with a ordinary stylus profilometer, a interferometric surface profiler (WYKO) and AFM. The ductile_mode grinding without brittle fracture is possible at higher table speed or larger speed ratio (table speed/wheel speed) for higher wheel speed. The surface roughness parallel to grinding direction attains to below 10nm (Ry) or below 2nm (Ra) with decreasing the table speed or the speed ratio. The surface roughness normal to grinding direction, on the other hand, is saturated to about 200nm (Ry). The wheel speed has little influence on the surface roughness normal to grinding direction.
Journal
-
- Journal of the Japan Society for Precision Engineering
-
Journal of the Japan Society for Precision Engineering 69 (11), 1595-1599, 2003
The Japan Society for Precision Engineering
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282679772829696
-
- NII Article ID
- 110001368360
-
- NII Book ID
- AN1003250X
-
- ISSN
- 1882675X
- 09120289
-
- NDL BIB ID
- 6756060
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- Abstract License Flag
- Disallowed